LEXAN™ EM3110R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VgIZ95_LEXAN-EM3110R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Automotive interiors. Optimizes flow/processability for cost effective thinner wall design uses. Internal mold release. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 90 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2170 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 210 | J/m | |
| -20°C | 590 | J/m | |
| 23°C | 640 | J/m | |
| 23°C, 6.40 mm | 210 | J/m | |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 56.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 127 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 118 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 124 | °C | |
| CLTE - Flow (-40 to 95°C) | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 254 to 277 | °C | |
| Middle Temperature | 266 to 288 | °C | |
| Front Temperature | 277 to 299 | °C | |
| Nozzle Temperature | 271 to 293 | °C | |
| Processing (Melt) Temp | 277 to 299 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE EE-2272N | Teknor Apex Company | TPE | Sarlink® TPE |
| Aricon™ 3150R15T1 | Technical Polymers, LLC | Polyester, TP | Aricon™ |
| Karina WHITE PVC COMPOUND 837-10/119-E-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PP EIP12030RF | Polykemi AB | PP+EPDM | POLYfill |
| ALTECH® PA6 A 4012/520 MR12 UV | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |