Eltex® PF6140AA

Category:	PE Copolymer , Polyethylene Copolymer
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VfGNCy_Eltex-PF6140AA.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Eltex® PF6140AA. is particularly suitable for high performance cast stretch film applications, in both monolayer and co-extruded structures. It also can be used for the production of artificial grass monofilaments.
Benefits and Features
Eltex® PF6140AA. is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:

High stretchability in cast stretch applications (up to 300%)

High holding force

Good web stability during extrusion

High output rates

Excellent overall film appearance and surface finish

Very high puncture resistance.

We recommend that you consult your INEOS technical representative for further advice on the use of Eltex® PF6130AA.

General Information
Additive	Antioxidant
Features	Antioxidant Copolymer Good Stretchability Good Surface Finish Hexene Comonomer Puncture Resistant
Uses	Cast Film Film
RoHS Compliance	Contact Manufacturer
Forms	Pellets
Processing Method	Cast Film Coextruded Film

Physical	Nominal Value	Unit	Test Method
Density ¹	0.918	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) ²(190°C/2.16 kg)	4.5	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	20	µm
Tensile Modulus			ISO 1184
1% Secant, MD : 20 µm	125	MPa
1% Secant, TD : 20 µm	120	MPa
Tensile Stress			ISO 1184
MD : Break, 20 µm	30.0	MPa
TD : Break, 20 µm	20.0	MPa
Tensile Elongation			ISO 1184
MD : Break, 20 µm	280	%
TD : Break, 20 µm	460	%
Dart Drop Impact (20 µm)	520	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm	310	g
TD : 25 µm	450	g

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 20.0 µm)	93		ASTM D2457
Haze (20.0 µm)	1.0	%	ASTM D1003

Additional Information	Nominal Value	Unit	Test Method
Puncture Resistance	27.0	Ncm/µ	Internal Method

Extrusion	Nominal Value	Unit
Melt Temperature	230 to 280	°C

Note Message
1 .	Conditioning ISO 1872/1
2 .	Condition 4

Resin Grade	Manufacturer	Category	Trademark
TOTAL Polypropylene PPH 3862	TOTAL Refining & Chemicals	PP Homopolymer	TOTAL Polypropylene
Aarolene® ARPP C 200-3	Aaron Industries Corp.	PP Copolymer	Aarolene®
Geon™ Vinyl Flexible R355AM	PolyOne Corporation	PVC+NBR	Geon™ Vinyl Flexible
PENTAMID A GV15 MA15 H LS black	PENTAC Polymer GmbH	Nylon 66	PENTAMID A
ESTOPLAST EP 4125GY81	Ester Industries Ltd.	PBT	ESTOPLAST EP