SABIC® LDPE 1808AN00
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VekVU1_SABIC-LDPE-1808AN00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 1808AN00 is an additive free autoclave grade with a low gel level, a high purity and a specific broad molecular weight distribution. The material can be processed at high speeds, thanks to it's excellent draw down properties and superior web stability. The grade has a very low gel level. SABIC® LDPE 1808AN00 combines high toughness with good flexibility and reasonable environmental stress cracking resistance and is therefore used for flexible and tough articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 7.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 25 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 10.0 | cm³/10min | ISO 1133 |
| 190°C/5.0 kg | 33.0 | cm³/10min | ISO 1133 |
| Environmental Stress-Cracking Resistance 1(60°C, 2.00mm, molded) | 2.00 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 160 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | |||
| Yield, 1.60mm, molded | 9.00 | MPa | ISO 527-2/200 |
| Yield, 2.00mm, molded | 8.00 | MPa | ISO 527-2/1BA/50 |
| Fracture, 1.60mm, molded | 14.0 | MPa | ISO 527-2/200 |
| Fracture, 2.00mm, molded | 12.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain | |||
| Fracture, 1.60mm, molded | 510 | % | ISO 527-2/200 |
| Fracture, 2.00mm, molded | 800 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 80.0 | MPa | ISO 899-1 |
| 1000 hr | 50.0 | MPa | ISO 899-1 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 9.00 | MPa | ISO 527-3 |
| TD : Yield, 25 µm | 8.00 | MPa | ISO 527-3 |
| MD : 25 µm | 13.0 | MPa | ISO 527-3 |
| TD : 25 µm | 10.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 300 | % | ISO 527-3 |
| TD : Break, 25 µm | 300 | % | ISO 527-3 |
| Water Vapor Transmission Rate (38°C, 100% RH, 25 µm) | 22 | g/m²/24 hr | Internal method |
| Oxygen Permeability (23°C, 25.0 µm) 2 | 0.90 | cm³/cm²/bar/24 hr | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 109 | J/g | DIN 53765 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Crack Resistance (25.0 µm) | 4000 | cycles/10 holes | Internal method |
| Tear Strength | ISO 6383-2 | ||
| MD : 25.0 µm | 10.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 8.0 | kN/m | ISO 6383-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/A |
| 23°C | 45 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 40.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 88.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 106 | °C | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| 2 . | 0% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSHINE PV300G4 | Polyram Ram-On Industries | ABS | RAMSHINE |
| RapidVac™ VA-258 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Zytel® PLUS PLSFR95G15DH2 BK269 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® PLUS |
| Kumho ABS HU651 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| VALOX™ V3900WX resin | SABIC Innovative Plastics Asia Pacific | PC+PBT | VALOX™ |