Tefzel® HT-2170
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | DuPont Fluoropolymers |
| Trademark: | Tefzel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VeeGEC_Tefzel-HT-2170.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DuPont™ Tefzel® fluoropolymer HT-2170 resin combines the chemical and high-temperature resistance of Tefzel® with antistatic levels of electrical conductivity. Tefzel® HT-2170 and the other Tefzel® fluoropolymers are melt processible, modified copolymers of ethylene and tetrafluoroethylene. They are high-performance resins that can be processed at relatively high rates compared to other fluorocarbon resins. They are mechanically tough and offer an excellent balance of properties. Tefzel® HT-2170 can perform successfully in applications where other thermoplastics are lacking in mechanical toughness, broad thermal capability, ability to meet difficult environmental conditions, or limited by fabricating problems. Properly processed products made from neat Tefzel® HT-2170 are inert to most solvents and chemicals, hydrolytically stable, and weather-resistant. The recommended upper service temperature is 150°C (302°F); useful properties are retained at cryogenic ranges. Mechanical properties include outstanding impact strength, cut-through, and abrasion resistance. The main advantage of Tefzel® HT-2170 is that it has improved stress crack resistance and flexibility when compared to other static-dissipating Tefzel® ETFE resins. To gain stress crack resistance, some physical strength has been sacrificed. Typical End Products Tefzel ® HT-2170 resin can be used to manufacture extruded tubing, pipe, and other profiles for hose; linings of components used in the chemical processing industries; industrial film; injection and blow-molded articles requiring superior electrical, chemical, and thermal properties and stress crack resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (297°C/5.0 kg) | 2.3 | g/10 min | ASTM D3159 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 200 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 220 - 250 | °C | ASTM D3418 |
| Maximum Service Temperature | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1 | 7.0 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Weather and Chemical Resistance: Excellent |
| Note Message | |
|---|---|
| 1 . | Volume resistivity as measured on compression molded plaques. Resistivity is very sensitive to processing technique. Injection molded plaques are typically higher. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 GB 10 TFE 13 SI2 | RTP Company | Nylon 66 | RTP |
| SUMILITE® PVC VSS-F110 | Sumitomo Bakelite Co., Ltd. | PVC, Unspecified | SUMILITE® PVC |
| NEFTEKHIM PE 2060V (60118) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| IROGRAN® A 70 H 4714 M | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| ESTOPLAST ZK 6220NN01 | Ester Industries Ltd. | PC | ESTOPLAST ZK |