Grivory® XE 4134 black 9225 is a Polyamide 10T/X Copolymer (Nylon 10T/X) material filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grivory® XE 4134 black 9225 are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 240 | 240 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | 1.6 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 11 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | 30 | kJ/m² | |
| 23°C | 30 | 30 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 280 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 165 | -- | °C | ISO 75-2/C |
| Maximum Use Temperature | Internal Method | |||
| Long Term | 150 | -- | °C | |
| Short Term | 250 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA 10T/X, MH, 12-100, GF30 | -- | ISO 1874 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 35 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.800 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® Rx1452 | Covestro - Polycarbonates | PC | Makrolon® |
| NuSil GEL-8100 | NuSil Technology | Silicone | NuSil |
| Grivory® GVX-65 H nat | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Hanwha Total PE E180F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |
| Kepamid® 1315GFH | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |