Dynacom 304
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Dynachem Co. Ltd. |
| Trademark: | Dynacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vdt4hu_Dynacom-304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Dynacom 304 is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific. Primary attribute of Dynacom 304: Flame Rated. |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.17 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 1.2 to 1.7 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 105 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 2 | 74.0 | 53.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 10 | 10 | % | ASTM D638 |
| Flexural Modulus 4 | 3330 | 1370 | MPa | ASTM D790 |
| Flexural Strength 5 | 108 | 61.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 44 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | -- | °C | ASTM D648 |
| Vicat Softening Temperature | 260 | -- | °C | ASTM D1525 6 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 26 | -- | kV/mm | ASTM D149 |
| Arc Resistance | 120 | -- | sec | ASTM D495 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.0313 mm) | V-0 | -- | UL 94 |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Conditioned Moisture Content | -- | 2.2 | % |
| Note Message | |
|---|---|
| 1 . | Thickness: 2 to 3 mm |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 3.0 mm/min |
| 6 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 2502AH | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| TechnoDur PBT 4 GF10 FR | TechnoCompound GmbH | PBT | TechnoDur |
| WPP PP PPC3GF1.5-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Karina GRAY PVC COMPOUND 902-18/71-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| neogol® 25 C UG | API SpA | TPO (POE) | neogol® |