MAXAMID™ N66-MOS3 BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VczVYA_MAXAMID-N66-MOS3-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™N66-MOS3 is a Nylon 66 with 3% Molybdenum Disulfied incorporated to provide excellent lubricity which significantly reduces the friction and improves the wear properties of injection molded parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3450 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 83.8 | °C | ASTM D648 |
| Melting Temperature | 254 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 290 to 305 | °C | |
| Mold Temperature | 38.0 to 93.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66HSL BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| Purell HP570U | LyondellBasell Industries | PP Homopolymer | Purell |
| TEREZ PMMA 5605 SZ | TER HELL PLASTIC GMBH | Acrylic (PMMA) | TEREZ PMMA |
| Desmovit® DP R 3914 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| LG PS 65IHE | LG Chem Ltd. | PS (HIPS) | LG PS |