陶氏低密度聚乙烯 615C
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VcGgtG_x-615C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ LDPE 615C is a Low Density Polyethylene Resin material. It is available in Latin America. Important attributes of DOW™ LDPE 615C are:
Typical application of DOW™ LDPE 615C: Food Contact Applications |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.20 to 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 12.0 | MPa | |
| TD : Yield, 38 µm | 12.0 | MPa | |
| MD : Break, 38 µm | 25.0 | MPa | |
| TD : Break, 38 µm | 22.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 300 | % | |
| TD : Break, 38 µm | 700 | % | |
| Dart Drop Impact (38 µm) | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 250 | g | |
| TD : 38 µm | 110 | g |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoTuff 420E | KMI Group Inc. | TPO (POE) | PrimoTuff |
| Sylvin 9909-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Adflex KS311P | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |
| Infino LS-3302 | SAMSUNG SDI CO., LTD. | PC | Infino |
| LUVOCOM® 1-7956 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |