Iupiace® GH30
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VbMXd3_Iupiace-GH30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupiace® GH30 is a Polyphenylene Ether + PS (PPE+PS) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupiace® GH30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 2.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Flow : 3.20 mm | 0.10 to 0.20 | % | |
| Water Absorption (Saturation, 23°C) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8900 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 103 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.3 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 176 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 136 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 2.5E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 30 | kV/mm | |
| 3.00 mm | 17 | kV/mm | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 260 to 290 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 270 to 310 | °C | |
| Mold Temperature | 90.0 to 125 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide BJ-37 Glass Reinforced High Impact | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| CONATHANE® EN-2521 | Cytec Industries Inc. | PUR, Unspecified | CONATHANE® |
| Fainplast PVC GSK 73/N-UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Sylvin 2910-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Clyrell RC5056 | PolyMirae | PP Random Copolymer | Clyrell |