LNP™ COLORCOMP™ HF1110C compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VZeKvG_LNPCOLORCOMPHF1110Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COLORCOMP* HF1110C is a general purpose Polycarbonate resin. Added features include: Good Clarity, Heat Resistant, Property Retention and Dimensional Stability. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C | 0.35 | % | ASTM D570 |
| Equilibrium, 100°C | 0.58 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 62.1 | MPa | ASTM D638 |
| Fracture | 65.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 120 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2310 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 54.2 | J | ASTM D3763 |
| Tensile Impact Strength 5 | 378 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 127 | °C | ASTM D648 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.1 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 249 - 271 | °C | |
| Middle Temperature | 260 - 282 | °C | |
| Front Temperature | 271 - 293 | °C | |
| Nozzle Temperature | 266 - 288 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 71 - 93 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Type S |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AECV Green T8L | Arkema | Nylon 12 | Rilsamid® |
| DN-Flex 5010N | DN Plastics | TPE | DN-Flex |
| Grilamid® XE 4108 nat | EMS-GRIVORY | Nylon 6/12 | Grilamid® |
| LEXAN™ 4704 resin | SABIC Innovative Plastics | PPC | LEXAN™ |
| Durez® 33183 | SBHPP | Phenolic | Durez® |