Plaslube® PES GF30 TL15
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VZ1Ki1_Plaslube-PES-GF30-TL15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® PES GF30 TL15 is a Polyethersulfone (PESU) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.15 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 125 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.19 | ||
| vs. Steel - Static | 0.16 | ||
| Wear Factor | 110 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 143 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 343 to 391 | °C | |
| Middle Temperature | 343 to 391 | °C | |
| Front Temperature | 343 to 391 | °C | |
| Processing (Melt) Temp | 332 to 388 | °C | |
| Mold Temperature | 138 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V70SW | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| SOLPLAST TC 5000D | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| Yuyao PPO N100B | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| KumhoSunny PC 2203I | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Lupoy® SC2302 | LG Chem Ltd. | PC | Lupoy® |