RELENE® E52009
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VYHPmh_RELENE-E52009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E52009 is a High Density Polyethylene (HDPE) grade with low gel content, excellent orientation characteristic and negligible water carry-over. This grade is recommended for making raffia tapes and monofilaments (Diameter >0.20 mm) with excellent balance of high tenacity and good elongation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm, Blown Film | 34.5 | MPa | |
| TD : Yield, 40 µm, Blown Film | 37.5 | MPa | |
| MD : Break, 40 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 45.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 900 | % | |
| TD : Break, 40 µm, Blown Film | 950 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 60 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, Blown Film | 24 | g | |
| TD : 40 µm, Blown Film | 68 | g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ALPHALOY MPC2501LG | Techno Polymer Co, Ltd. | PC+ABS | TECHNO ALPHALOY |
| Elvacite® 2045 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| Kumho SAN SAN 310TR | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |
| Sylvin 8225-80 Brown 7428 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ PF008S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |