LNP™ LUBRICOMP™ ZFG26 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VWKwLZ_LNPLUBRICOMPZFG26compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZFG26 is a compound based on PPE+PS Blend resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound ZFL-4326 Product reorder name: ZFG26 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.42 | g/cm³ | ASTM D792 |
| -- | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.73 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.36 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13100 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 110 | MPa | ASTM D638 |
| Yield | 109 | MPa | ISO 527-2 |
| Fracture | 115 | MPa | ASTM D638 |
| Fracture | 109 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 1.5 | % | ASTM D638, ISO 527-2 |
| Fracture | 1.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 10500 | MPa | ASTM D790 |
| -- | 10000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 165 | MPa | ASTM D790 |
| -- | 163 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.62 | ASTM D3702 Modified | |
| With Self-Static | 0.89 | ASTM D3702 Modified | |
| Wear Factor - Washer | 113 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 2 | 8.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.30 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 140 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 135 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 2.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu ML1220 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| HiFill FR® PA6 GF13 FR-N IM BK | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| Huafon JF-S-8080A | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Vipel® F701-RTP-13 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Paryls® PPSU K1565 | Youju New Materials Co., Ltd. | PPSU | Paryls® |