ACCUCOMP™ POL055UVL
| Category: | PC , Polycarbonate |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VWGC7W_ACCUCOMP-POL055UVL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACCUCOMP™ POL055UVL is a Polycarbonate (PC) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 75.0 | MPa | |
| Break | 75.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 170 | % | |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 770 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 140 | °C | |
| 1.8 MPa, Unannealed | 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS-351T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| NAXELL™ PC23M-10G | MRC Polymers, Inc. | PC | NAXELL™ |
| NuSil R-2180-2 | NuSil Technology | Silicone | NuSil |
| Hydroxy-Purge 8C | InChem Corp. | TP, Unspecified | Hydroxy-Purge |
| LEXAN™ 203R resin | SABIC Innovative Plastics | PC | LEXAN™ |