EMERGE™ PC 8702-10
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VW5UVw_EMERGE-PC-8702-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8702 Advanced Resin is an ignition-resistant, 20% glass reinforced, polycarbonate resin. This resin contains no bromine, chlorine, or phosphate additives. The resin is designed to meet the German norm DIN VDE-0472/Part 815 (1989) on halogens. It is a medium flow PC resin with a mold release system, intended for injection molding applications. Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 4000 | MPa | ASTM D638 |
| Tensile Strength (Break, 3.20 mm, Injection Molded) | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 5380 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 145 | °C | |
| 1.8 MPa, Unannealed | 140 | °C | |
| 1.8 MPa, Annealed | 143 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+14 | ohms | ASTM D257 |
| Volume Resistivity (1.80 mm) | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 27 | kV/mm | ASTM D149 |
| Dielectric Constant (1.60 mm, 1 MHz) | 3.10 | ASTM D150 | |
| Comparative Tracking Index (3.00 mm) | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1(1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 79.4 to 116 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PPR PPCO04 | Premier Plastic Resins, Inc. | PP Copolymer | PPR |
| Sylvin 8299-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DOWLEX™ IP 40 | The Dow Chemical Company | HDPE | DOWLEX™ |
| FRIANYL® A GF25 V0P3 | Nilit Plastics | Nylon 66 | FRIANYL® |
| LNP™ LUBRICOMP™ KG002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |