STYRON A-TECH™ 1110
| Category: | PS (HIPS) , Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON A-TECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VVv2v9_STYRON-A-TECH-1110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON A-TECH™ 1110 advanced technology polystyrene resin is a high-gloss, high-impact resin for injection molding applications. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| -- | 1030 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (200°C/5.0 kg) | 4.00 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| Compression Molded | 1750 | MPa | ASTM D638 |
| Injection Molded | 1860 | MPa | ASTM D638 |
| -- | 1770 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield, Compression Molded | 20.7 | MPa | ASTM D638 |
| Yield, Injection Molded | 22.8 | MPa | ASTM D638 |
| Yield | 25.0 | MPa | ISO 527-2 4 |
| Break, Compression Molded | 14.5 | MPa | ASTM D638 |
| Break, Injection Molded | 19.3 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield | 1.5 | % | ISO 527-2 5 |
| Break, Compression Molded | 30 | % | ASTM D638 |
| Break, Injection Molded | 50 | % | ASTM D638 |
| Nominal strain at break | > 50 | % | ISO 527-2 6 |
| Flexural Modulus | ASTM D790 | ||
| Compression Molded | 1900 | MPa | |
| Injection Molded | 2140 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Compression Molded | 38.3 | MPa | |
| Injection Molded | 44.8 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 7 | ||
| -30°C | 4.00 | kJ/m² | |
| 23°C | 18.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 8 | ||
| -30°C | 60.0 | kJ/m² | |
| 23°C | 125 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, Compression Molded | 130 | J/m | |
| 23°C, Injection Molded | 240 | J/m | |
| Gardner Impact (23°C) | 33.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa | 87.0 | °C | ISO 75-2 9 |
| 1.8 MPa, Unannealed | 72.8 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 92.8 | °C | ASTM D648 |
| 1.8 MPa | 76.0 | °C | ISO 75-2 10 |
| Vicat Softening Temperature | |||
| -- | 102 | °C | ASTM D1525 |
| 50°C/h, B (50N) | 88.0 | °C | ISO 306 11 |
| CLTE - Flow | |||
| -- | 7.6E-5 | cm/cm/°C | ASTM D696 |
| -- | 8.6E-5 | cm/cm/°C | ISO 11359-2 12 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 13(1.50 mm) | HB | UL 94 | |
| Burning Behav. at thickness h (3.10 mm, UL) | HB | ISO 1210 14 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 92 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 HI | RTP Company | PP, Unspecified | RTP |
| ACCUTECH™ HP0336C30L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Ducor® 1101 P | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| INNOPOL® PP CS 1-2820 MA | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Karina STRAW PVC COMPOUND 800-38/39-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |