LUBLENE GC30 NATURAL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBLENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VUkQCS_LUBLENE-GC30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PP natural first choice. With glass fibres and coupling agents. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 to 1.14 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 to 5500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 65.0 to 75.0 | MPa | |
| Break | 65.0 to 75.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 2.5 to 3.0 | % | |
| Break | 2.5 to 3.0 | % | |
| Flexural Modulus 1 | 4000 to 5000 | MPa | ISO 178 |
| Flexural Stress 2 | 70.0 to 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 to 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 to 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 80 to 90 | J/m | ASTM D256A |
| 23°C 3 | 40 to 50 | kJ/m² | ASTM D256 |
| 23°C | 8.0 to 9.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 8.0 to 9.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 40 to 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 to 155 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 145 to 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 130 to 140 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 155 to 165 | °C | ISO 306/A120 |
| -- | 125 to 135 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1207-90A | RTP Company | TPU-Polyester | RTP |
| Spartech Polycom PP5120C B3-R | Spartech Polycom | PP, Unspecified | Spartech |
| Karina CLEAR PVC COMPOUND 78/200-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| 3M™ Dyneon™ Fluoroelastomer FE 5622Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Sylvin 2900-80 Clear 8382 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |