KOPA® KN181D
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VSi3Y6_KOPA-KN181D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KOPA® KN181D is a Polyamide 6 (Nylon 6) product. It is available in Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.3 to 1.5 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 1.8 | % | ASTM D570 |
| Comonomer Content | < 0.8 | % | |
| Moisture Content | < 1000 | ppm | |
| Relative Viscosity 1 | 2.6 to 2.7 | ||
| Color b | -3.80 to 1.80 | ||
| Color L | 70.0 to 78.0 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Amino End Groups | 42 to 62 | meq/kg |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 76.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 46 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2780 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 180 | °C | |
| 1.8 MPa, Unannealed | 65.0 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 96% H2SO4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ShinkoLite-P IR D-70 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| NOVALAC FM 4017F | Vyncolit N.V. | Phenolic | NOVALAC |
| Nycal™ 2155R33 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Globalene® SI4101 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| EPO-TEK® OG116 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |