LNP™ THERMOCOMP™ DF0049P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VS6beN_LNP-THERMOCOMP-DF0049P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF0049P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DF-1004 EP FR Product reorder name: DF0049P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6850 | MPa | ASTM D638 |
| -- | 6950 | MPa | ISO 527-2/1 |
| Tensile Strength (Break) | 108 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6090 | MPa | ASTM D790 |
| -- | 6210 | MPa | ISO 178 |
| Flexural Strength | 165 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 7.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D4812 |
| 23°C 3 | 48 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.4 | J | ASTM D3763 |
| -- | 9.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 135 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.850 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 AR 20 | RTP Company | PPA | RTP |
| Sylvin 8716-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| APEX® RE 8114 UV | Teknor Apex Company | PVC, Rigid | APEX® |
| INEOS HDPE T60-500-119 | INEOS Olefins & Polymers USA | HDPE | INEOS HDPE |
| PENTAMID B MA 25 H schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |