Bio-Flex® A 4100 CL
| Category: | PLA , Polylactic Acid |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VRZcPf_Bio-Flex-A-4100-CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bio-Flex® A 4100 CL is a Polylactic Acid (PLA) material. It is available in Europe for film extrusion. Primary attribute of Bio-Flex® A 4100 CL: Eco-Friendly/Green. Typical application of Bio-Flex® A 4100 CL: Film |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Apparent Density | 0.82 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 to 10 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 5.50 to 9.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1840 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 22.0 | MPa | ISO 527-2 |
| -- | 44.0 | MPa | ISO 527 |
| Tensile Strain (Break) | 12 | % | ISO 527-2 |
| Flexural Modulus | 1770 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 48.0 | MPa | ISO 178 |
| Flexural Strain at Break | No break | % | ISO 178 |
| Tensile Strain at Tensile Strength | 5.0 | % | ISO 527 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Nitrogen Transmission Rate (25 µm) | 65.0 | cm³/m²/24 hr | DIN 53380-2 |
| Oxygen Transmission Rate (20 µm) | 130 | cm³/m²/24 hr | ISO 15105-2 |
| Water Vapor Transmission 1 | 170 | g/m²/24 hr | ISO 15106-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 44 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 40.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 44.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | > 155 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 20µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PC/ABS CW-G20 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC+ABS | Zhongfa |
| NYLOY® GT-0010N ST | Nytex Composites Co., Ltd. | PLA | NYLOY® |
| Fiberfil® PP-60/TC/40 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Lifolit® E 75.0898/1 | ELASTO | PVC, Flexible | Lifolit® |
| Sylvin 9080-75 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |