Karina BLACK PVC COMPOUND -E 807D48/ 1-C-IS
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VR1baq_Karina-BLACK-PVC-COMPOUND--E-807D48-1-C-IS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PVC COMPOUND CLASS 70C (PVC/F AND ST1) RECOMMENDED FOR INSULATION AND JACKETING OF ELECTRICAL FLEXIBLE WIRES AND CABLES. ALSO RECOMMENDED FOR COAXIAL JACKETING AND PLUG INJECTION. LEAD STABILIZED COMPOUND. |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.33 to 1.39 | g/cm³ | IEC 60811-1-3 |
| Color | OK | ME 12 | |
| Color a | -0.850 to 0.750 | ME 12 | |
| Color b | -1.29 to 0.310 | ME 12 | |
| Color L | 25.4 to 27.0 | ME 12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 to 82 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -26.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | NBR 5403 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL4M 850 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Zytel® HTN 52G35HSL BK083 | DuPont Performance Polymers | PPA | Zytel® HTN |
| AIE PBT 30G3 | Asia International Enterprise (Hong Kong) Limited | PBT | AIE PBT |
| Daicel PP PG8N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Later 4 G/30-V0CT2 | LATI S.p.A. | PBT | Later |