FARALLOY® PE-204
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | O'Neil Color and Compounding |
| Trademark: | FARALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VQUxgY_FARALLOY-PE-204.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FARALLOY PE-204 is a talc filled extrusion compound designed to increase the heat deflection properties while maintaining a high impact strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 86.1 | °C | |
| 0.45 MPa, Annealed | 107 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ETILINAS HD5218AA | POLYETHYLENE MALAYSIA SDN BHD | HDPE | ETILINAS |
| Karina IVORY PVC COMPOUND 70900-35/ 1-J-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina PINK COLOR CONCENTRATE 39/322-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Dapol® D500 | Fudow Co., Ltd. | DAP | Dapol® |
| LEXAN™ 143 resin | SABIC Innovative Plastics | PC | LEXAN™ |