KOPA® KN333HI5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VQCe4i_KOPAKN333HI5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPA®KN333HI5 is a polyamide 66 (nylon 66) product,. It can be processed by injection molding and is available in North America, Latin America, Europe or Asia Pacific. KOPA®KN333HI5 applications include electrical/electronic applications, engineering/industrial accessories and the automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.6 - 1.9 | % | ASTM D955 |
| Transverse flow | 2.0 | % | ISO 294-4 |
| Flow | 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 2.7 | % | ISO 62 |
| Balanced, 23°C, 60% RH | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 110 | ASTM D785 | |
| R scale | 113 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23% strain | 59.0 | MPa | ASTM D638 |
| 23°C | 60.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 50 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2260 | MPa | ASTM D790 |
| 23°C | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 88.0 | MPa | ASTM D790 |
| 23°C | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 66.3 | °C | ISO 75-2/A |
| Melting Temperature | 255 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.10 | ASTM D150 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80 - 100 | °C | |
| Drying Time - Desiccant Dryer | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 260 | °C | |
| Front Temperature | 265 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G15 202 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Supol HT144HE | LyondellBasell Industries | PP Copolymer | Supol |
| NYCOA Polyamide 5100 HS | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| EVATHENE® UE638-04 | USI Corporation | EVA | EVATHENE® |
| Lushan VB150A | Guangzhou Lushan New Materials Co., Ltd | PE, Unspecified | Lushan |