Boda BDP-HL9701

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	Chenguang Fluoro & Silicone Elastomers Co., Ltd.
Trademark:	Boda
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VQAiAD_Boda-BDP-HL9701.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Material Type: Black color low viscosity fluoroelastomer compound, hardness Shore
A 65~75. Based on peroxide curable fluoroelastomer with very high fluorine content which brings outstanding chemicals resistance properties.

Features:

Short post cure time

Excellent mold flow and mold release, resulting in less flash

Extraordinary chemical resistance:

Alcohol Fuel

Steam

Acids

Chemicals containing amines.

Process Methods: Suitable for compression, transfer, injection and extrusion molding processes.

Applications: For O-rings, gaskets used in chemical and petrochemical industries.

Lab Testing Curing Condition:

Press Curing: 10min@170°C.

Oven: (1+4)hrs@230°C

General Information
Features	Acid Resistant Alcohol Resistant Fuel Resistant Good Chemical Resistance Good Flow Good Mold Release Good Moldability Low Viscosity Minimal Flash Steam Resistant
Uses	Gaskets
Appearance	Black
Processing Method	Compression Molding Extrusion Injection Molding Resin Transfer Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.98	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	72		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	23.7	MPa	ASTM D412
Tensile Elongation (Break)	240	%	ASTM D412
Compression Set ¹(200°C, 70 hr)	23	%	ASTM D395

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air (250°C, 70 hr)	-4.0	%	ASTM D573
Change in Ultimate Elongation in Air (250°C, 70 hr)	-10	%	ASTM D573
Change in Durometer Hardness in Air (250°C, 70 hr)	1.0		ASTM D573
Change in Tensile Strength (23°C, 70 hr, in Reference Fuel C)	-10	%	ASTM D471
Change in Ultimate Elongation (23°C, 70 hr, in Reference Fuel C)	-12	%	ASTM D471
Change in Durometer Hardness (23°C, 70 hr, in Reference Fuel C)	2.0		ASTM D471
Change in Volume (23°C, 70 hr, in Reference Fuel C)	1.0	%	ASTM D471

Note Message
1 .	6 mm Buttons

Resin Grade	Manufacturer	Category	Trademark
SILPURAN® 2438 ADH A/B	Wacker Chemie AG	Silicone	SILPURAN®
Carbotex KGN-30MRA	Kotec Corporation	PC	Carbotex
Arnite® T04 200	DSM Engineering Plastics	PBT	Arnite®
COPYLENE® CM350LN	Phillips 66	PP Impact Copolymer	COPYLENE®
Karina CLEAR PVC COMPOUND -E 80/274-IS-RG	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina