Order Products : sales@su-jiao.com
BESTPOM C09U/02
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VOyZZa_BESTPOM-C09U-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Acetal Copolymer resin black standard MFI 9, lubrified and with stabilization against ultra violet radiations (UV), is perfect for exterior pieces or in contact with external atmospheric agents. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 2.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2950 | MPa | ISO 527-2 |
| Tensile Stress | 64.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 65 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 165 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 4.00 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 FRC 3 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| ACRYREX® CM-207 | CHI MEI CORPORATION | Acrylic (PMMA) | ACRYREX® |
| Celstran® PA66-GF50-02 AD3007 | Celanese Corporation | Nylon 66 | Celstran® |
| HiFill® ABS E GM5 LE | Techmer Engineered Solutions | ABS | HiFill® |
| LNP™ THERMOCOMP™ WB006 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |