LEXAN™ 925A resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VORW9g_LEXAN-925A-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lexan* 925A Polycarbonate (PC) resin is a non-filled, injection moldable grade of non-chlorinated, non-brominated flame retardant systems that has an UL-94 V0 rating. Lexan 925A is available in transparent and tinted color options and is a general-purpose resin ideal for a wide variety of applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 63.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 85 | % | |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 73 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 135 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 124 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ISO 306/B50 |
| -- | 142 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 7.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | ||
| 60 Hz | 2.70 | ||
| 1 MHz | 2.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 0.010 | ||
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ISO 489 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 sp=62mm |
| 5 . | 80*10*3 |
| 6 . | 80*10*3 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2256 | Covestro - Polycarbonates | PC | Makrolon® |
| Sarlink® TPV X23080N | Teknor Apex Company | TPV | Sarlink® TPV |
| TOTAL Polypropylene PPC 5720WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| LNP™ LUBRICOMP™ DFP32 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Hostacom ERC 204N C11354 | LyondellBasell Industries | PP Copolymer | Hostacom |