RTP 103
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VMNyuX_RTP-103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4480 | MPa | ASTM D638 |
| Tensile Strength | 46.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 149 | °C | |
| 1.8 MPa, Unannealed | 121 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXTEL® 650-BK | MRC Polymers, Inc. | PP Homopolymer | MAXTEL® |
| NatureFlex™ 90NVS | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| CALIBRE™ 200-3 | Trinseo | PC | CALIBRE™ |
| MARPOL® LL6F 801-HSB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Dryflex® SE 80A301 | ELASTO | TPE | Dryflex® |