LUBAN™ 1128 N
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) |
| Trademark: | LUBAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VIyBp1_LUBAN-1128-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Luban polypropylene is manufactured using Novolen vertical stirred gas-phase polymerization process. 1128 N is a homopolymer polypropylene with superior slip and antiblocking properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | DIN 53121 | ||
| Across Flow : 0.0500 mm | 760 | MPa | |
| Flow : 0.0500 mm | 700 | MPa | |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.18 | DIN 53375 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Elongation | DIN 53455 | ||
| Break, 50 µm, Cast Film | 680 | % | |
| TD : Break, 50 µm, Cast Film | 720 | % | |
| Dart Drop Impact 1(50 µm, Cast Film) | 280 | g | ASTM D1709 |
| Trouser Tear Resistance | DIN 53455 | ||
| MD : 50 µm, Cast Film | 42.0 | N/mm | |
| TD : 50 µm, Cast Film | 38.0 | N/mm |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm, Cast Film) | 100 | ISO 2813 | |
| Haze (50.0 µm, Cast Film) | 2.7 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 4175 | Teknor Apex Company | TPV | Sarlink® TPV |
| Torelina® AR10M | Toray Resin Company | PPS | Torelina® |
| AKROMID® B3 3 S3 10 natural (1808) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Bergadur™ PB40 G10 NC007 | PolyOne Corporation | PBT | Bergadur™ |
| Asrene® SP 4808 | Chandra Asri Petrochemical | HDPE | Asrene® |