| Mineral reinforced Scratch resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 to 1.5 | % | |
| Flow | 1.3 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 21.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 8.0 | % | |
| Break | 25 | % | |
| Flexural Modulus (23°C) | 1500 | MPa | ISO 178 |
| Flexural Stress | 36.0 | MPa | ISO 178 |
| Scratch Resistance - 10 N Fine Structure 1 | < 0.100 | dL | ISO 1518/D65 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 45 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2 | |||
| 0.45 MPa, Unannealed | 108 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 to 1.0E-4 | cm/cm/°C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Test performed on black plaques with fine (Standex MT9078) and rough (Standex MT11435) structure |
| 2 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SynPlast™ DOA-FM | PolyOne Corporation | Di (2-ethylhexyl) Adipate | SynPlast™ |
| Chemical Resources GPPS1500 | Chemical Resources, Inc. | PS (GPPS) | Chemical Resources |
| Diakon® CLG902L | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Genestar™ G1350H | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| LUVOCOM® 50/CF/7/GS/10/TF/5/EM/BK 100 | LEHVOSS Group | PC | LUVOCOM® |