EVATHENE® UE632

Category:	EVA , Ethylene Vinyl Acetate Copolymer
Manufacturer:	USI Corporation
Trademark:	EVATHENE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VGl6Z6_EVATHENE-UE632.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
UE632 is a high VA content ethylene-vinyl acetate copolymer(EVA) with excellent low temperature impact strength, environmental stress crack resistance, flexibility, elasticity, transparency, and easy processability. It could be developed for many new applications and substitute for flexible PVC, rubbers, and other elastomers. One of major application of UE632 is incorporated with blowing agent and cross-linking agent for compression molding or injection molding of foamed shoe sole. Besides, UE632 could be processed by profile extrusion, injection molding, and blown-extrusion while incorporated with additives.

Message

UE632 is a high VA content ethylene-vinyl acetate copolymer(EVA) with excellent low temperature impact strength, environmental stress crack resistance, flexibility, elasticity, transparency, and easy processability. It could be developed for many new applications and substitute for flexible PVC, rubbers, and other elastomers. One of major application of UE632 is incorporated with blowing agent and cross-linking agent for compression molding or injection molding of foamed shoe sole. Besides, UE632 could be processed by profile extrusion, injection molding, and blown-extrusion while incorporated with additives.

General Information
Features	Copolymer Good Flexibility Good Processability High Clarity High Elasticity High ESCR (Stress Crack Resist.) Low Temperature Strength
Uses	Foam Footwear Profiles
Processing Method	Compression Molding Extrusion Foam Processing

Physical	Nominal Value	Unit	Test Method
Density	0.942	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR)	2.2	g/10 min	ASTM D1238
Vinyl Acetate Content	22.0	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	34		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	16.7	MPa	ASTM D638
Tensile Elongation (Break)	820	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746
Vicat Softening Temperature	58.0	°C	ASTM D1525
Peak Melting Temperature	82.0	°C	ASTM D3418

Resin Grade	Manufacturer	Category	Trademark
TEKAPPO™ J910	Mando Advanced Materials Co., Ltd.	PPE+PS	TEKAPPO™
Generic Nylon 66 - Carbon Fiber, Long	Generic	Nylon 66	Generic
Hostaform® EC140XF	Celanese Corporation	Acetal (POM) Copolymer	Hostaform®
LNP™ STAT-LOY™ W3000XXJ compound	SABIC Innovative Plastics	PBT	LNP™ STAT-LOY™
PLUSTEK PA303G4	Polyram Ram-On Industries	Nylon 66	PLUSTEK