POLYLAC® PA-747H
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VGaHeP_POLYLAC-PA-747H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-747H is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 0.23 | g/10 min | |
| 220°C/10.0 kg | 2.8 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(6.00 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(6.00 mm) | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.00 mm | 440 | J/m | |
| 23°C, 6.00 mm | 310 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 85.0 | °C | |
| 1.8 MPa, Annealed | 95.0 | °C | |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 210 | °C | |
| Cylinder Zone 3 Temp. | 210 to 240 | °C | |
| Cylinder Zone 5 Temp. | 220 to 250 | °C | |
| Die Temperature | 200 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| reSound™ X RS1200-0215 | PolyOne Corporation | PLA Comp | reSound™ |
| TAROPRENE® 1 A85 M1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Wellamid® GF43-66/6 XE-NBK1 | Wellman Engineering Resins | Nylon 66/6 | Wellamid® |
| Geon™ Vinyl Flexible XV3906 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Cellasto® MH24-35 | BASF Polyurethanes GmbH | TPU, Unspecified | Cellasto® |