Propafilm™ RXD140
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VG5fXx_Propafilm-RXD140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Barrier Coated Film Biaxially oriented polypropylene (BOPP) film coated on both sides with an aqueous dispersion of polyvinylidene chloride (PVdC) copolymer. RXD110/130/140 are recommended for use in plain and printed overwrapping applications in the cookie and bakery industries. Also suited for use as a single web or in laminate structures for medium to large packs on form-fill-seal machines. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3600 | µm | |
| Seal Strength 1 | 0.14 | N/mm | Internal Method |
| Seal Initiation Temperature 2 | 93.3 to 146 | °C | Internal Method |
| Oxygen Permeability (25°C, 0% RH) | 0.38 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 3.3 | g/m²/24 hr | ASTM F1770 |
| Yield | 29.1 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 110 | ASTM D2457 | |
| Haze 3 | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2secs; 15psi |
| 2 . | 2secs; 15psi |
| 3 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DAPCO™ 3003 | Cytec Industries Inc. | Epoxy | DAPCO™ |
| DuraElast 1730-70 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraElast |
| Elastollan® R 2000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| LUVOCOM® 1-3260/NC | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Hifax TYC 1190P 3004 BLACK | LyondellBasell Industries | TPO (POE) | Hifax |