NAXALOY® 793A7
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXALOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VG1aSF_NAXALOY-793A7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 793A7 is available in natural and custom colors, internal and external lubricants, UV stabilizer and other modifications. Further information and details are available upon request. |
| General Information | |
|---|---|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.50 to 0.80 | % | |
| Across Flow : 3.20 mm | 0.70 to 0.90 | % | |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, 3.20 mm) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm) | 2140 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm) | 83.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 132 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 115 | °C | |
| CLTE - Flow (-40 to 35°C) | 6.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XT-507 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| LARIPUR® LPR 5450 | COIM S.p.A. | TPU-Polyether | LARIPUR® |
| Karina IVORY TR (SP31503) -E TR-600N35/ 1-YT-A | Karina Ind. e Com. de Plásticos Ltda | TPE | Karina |
| POLIMAXX 2440TC | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| Badaflex® TPU 80A 8049 GK20 S1 | Bada AG | TPU, Unspecified | Badaflex® |