MAZMID B 150 FV 50
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. |
| Trademark: | MAZMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VFEEgi_MAZMID-B-150-FV-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAZMID B 150 FV 50 is a Polyamide 6 (Nylon 6) product filled with 50% glass fiber. It can be processed by injection molding and is available in Latin America. Applications of MAZMID B 150 FV 50 include electrical/electronic applications, engineering/industrial parts, automotive and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.56 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.25 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.75 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | 115 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 14500 | 700 | MPa | ASTM D638 |
| Tensile Strength | 200 | 140 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | 3.0 | % | ASTM D638 |
| Flexural Modulus | 13000 | 8000 | MPa | ASTM D790 |
| Flexural Strength | 300 | 190 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 130 | 230 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 230 | -- | °C | |
| 1.8 MPa, Unannealed | 220 | -- | °C | |
| Continuous Use Temperature | 120 to 130 | -- | °C | |
| Melting Temperature | 214 to 220 | -- | °C | |
| CLTE - Flow | 1.8E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3760 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SCHULADUR® A GB 20 | A. Schulman Europe | PBT | SCHULADUR® |
| TRIBOCOMP® PC GF30 TS0 | EPIC Polymers | PC | TRIBOCOMP® |
| Karina WHITE PVC COMPOUND -E 803-10/ 1-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TAFMER™ PN-0040 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |