SABIC® PP 612MK10
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VCDzrI_SABIC-PP-612MK10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This grade is especially developed for Pails and Containers. Special characteristics of this grade are a high crystalisation temperature, very high flow in combination with medium impact performance and low taste influences. This enables outstanding processability, very easy mould filling, short cycle times and an optimal grade for food-contact applications. SABIC® PP 612MK10 is like all SABIC® PP products formulated to allow trouble free processing. The material is also available in an antistatic version. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 33 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 140 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 2.00mm | 27.0 | MPa | ISO 527-2/50 |
| Fracture, 2.00mm | 18.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 2.00 mm) | 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1450 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 4.0 | kJ/m² | ISO 179 |
| 0°C | 5.5 | kJ/m² | ISO 179 |
| 23°C | 9.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180/A | ||
| -20°C | 4.0 | kJ/m² | ISO 180/A |
| 0°C | 5.0 | kJ/m² | ISO 180/A |
| 23°C | 8.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 102 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Additional Information |
|---|
| Strain at Break, ISO 527, 2mm, 50mm/min: >50% |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C 3513 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Network Polymers PP PPB 25 1316 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Durez® 31906 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| TECHNYL® A 216 V15 BLACK 21N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Sylvin 9772-75 Grey 9222 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |