DOWLEX™ 5075G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V9I9rt_DOWLEX-5075G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX 5075G Polyethylene Resin is a blown film extrusion linear low density polyethylene resin grade suitable for high toughness and clarity film applications.. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 4.96 | J | Internal method |
| Film Puncture Force | 56.8 | N | Internal method |
| Film Puncture Resistance | 22.5 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 94.6 | J/cm³ | ASTM D882 |
| TD | 92.1 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 185 | MPa | ASTM D882 |
| 2% secant, MD | 154 | MPa | ASTM D882 |
| 1% secant, TD | 219 | MPa | ASTM D882 |
| 2% secant, TD | 185 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.1 | MPa | ASTM D882 |
| TD : Yield | 11.0 | MPa | ASTM D882 |
| MD : Fracture | 44.3 | MPa | ASTM D882 |
| TD : Fracture | 34.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 510 | % | ASTM D882 |
| TD : Fracture | 590 | % | ASTM D882 |
| Dart Drop Impact | 400 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 450 | g | ASTM D1922 |
| TD | 590 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 118 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 64 | ASTM D2457 | |
| Haze | 7.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 213 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Die Size: 8 in. Screw Type: DSB II Die Gap: 70mil (1.8 mm) Melt Temperature: 416°F (223°C) Output: 12 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 44.3 rpm Frost Line Height: 45 in. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-9611U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| TORZEN® G4000HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| YUCLAIR® MK910 | SK Global Chemical | HDPE | YUCLAIR® |
| Indothene HD 50MA045 | Reliance Industries Limited | HDPE | Indothene HD |
| DEXFLEX® 727 RXF | LyondellBasell Industries | TPO (POE) | DEXFLEX® |