LOFEX® A5110
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | LOFEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V8wM40_LOFEX-A5110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LOFEX ® A5110 Polyester film is hazy and one side corona treated with excellent properties by tensile strength, proper elongation and the thermal contraction rate. It can use by release film because it has excellent run, easy treatment by suitable product. Also, it is a product that thickness control is possible according to customer needs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Tension | |||
| 50.0 µm | 52 | mN/m | |
| 75.0 µm | 52 | mN/m | |
| 100.0 µm | 52 | mN/m |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| F5 | ASTM D882 | ||
| MD : 50.0 µm | 113 | MPa | |
| MD : 75.0 µm | 113 | MPa | |
| MD : 100.0 µm | 113 | MPa | |
| TD : 50.0 µm | 113 | MPa | |
| TD : 75.0 µm | 113 | MPa | |
| TD : 100.0 µm | 113 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Shrinkage | Internal Method | ||
| MD, 30 min : 150°C, 50.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 75.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 100.0 µm | 1.0 | % | |
| TD, 30 min : 150°C, 50.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 75.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 100.0 µm | 0.50 | % | |
| Surface Treatment | Inside (Corona) |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 196 | MPa | |
| MD : Yield, 75 µm | 196 | MPa | |
| MD : Yield, 100 µm | 196 | MPa | |
| TD : Yield, 50 µm | 235 | MPa | |
| TD : Yield, 75 µm | 216 | MPa | |
| TD : Yield, 100 µm | 216 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 170 | % | |
| MD : Break, 75 µm | 170 | % | |
| MD : Break, 100 µm | 170 | % | |
| TD : Break, 50 µm | 120 | % | |
| TD : Break, 75 µm | 120 | % | |
| TD : Break, 100 µm | 120 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60°, 50.0 µm | 150 | ||
| 60°, 75.0 µm | 150 | ||
| 60°, 100 µm | 150 | ||
| Transmittance | ASTM D1003 | ||
| 50.0 µm | 87.0 | % | |
| 75.0 µm | 87.0 | % | |
| 100 µm | 87.0 | % | |
| Haze | ASTM D1003 | ||
| 50.0 µm | 3.8 | % | |
| 75.0 µm | 5.3 | % | |
| 100 µm | 9.5 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 MS 1 EG | RTP Company | Acetal (POM) Copolymer | RTP |
| UNITIKA Nylon 66 B2040G50 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| NEXUS PC/ABS PC/ABSQX7002 | Nexus Resin Group, LLC. | PC+ABS | NEXUS PC/ABS |
| BESTNYL SE30VI02AS08 | Triesa Plastics | Nylon 66 | BESTNYL |
| TOTAL Polystyrene Impact 5240 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |