KumhoSunny PA/ABS HNA0370
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PA/ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V8qNs8_KumhoSunny-PA-ABS-HNA0370.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HNA 0370 has the feature of high impact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 240°C/10.0 kg | 45 to 60 | g/10 min | ASTM D1238 |
| 240°C/10.0 kg | 60 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.60 to 0.80 | % | ASTM D955 |
| -- | 0.60 to 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 48.0 | MPa | ASTM D638 |
| -- | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 1800 | MPa | ASTM D790 |
| -- 1 | 1600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 72.0 | MPa | ASTM D790 |
| -- 2 | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact | |||
| 3.20 mm | 200 | J/m | ASTM D256 |
| 23°C 4 | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 102 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ASTM D1525 6 |
| -- | 115 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4J |
| 4 . | 5.5J |
| 5 . | 120°C/h |
| 6 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ TR-818.G001-8081 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Sumitomo Epoxy E 8353-706R-1 | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| Vyncolit® 3615CG | Vyncolit N.V. | Phenolic | Vyncolit® |
| Kynar Flex® 2850 Black | Arkema | PVDF | Kynar Flex® |
| LEXAN™ HF1110 resin | SABIC Innovative Plastics | PC | LEXAN™ |