Generic Nylon 66
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V7x2Id_Generic-Nylon-66.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 - 1.18 | g/cm³ | ASTM D792 |
| 23°C | 1.03 - 1.21 | g/cm³ | ISO 1183 |
| -- | 1.14 - 1.15 | g/cm³ | ASTM D1505 |
| Apparent Density | |||
| -- | 0.67 - 0.70 | g/cm³ | ASTM D1895 |
| -- | 0.70 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 235°C/1.0 kg | 9.3 - 35 | g/10 min | ASTM D1238 |
| 275°C/0.325 kg | 2.0 - 5.1 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.2 - 1.8 | % | ASTM D955 |
| Transverse flow : 23°C | 0.79 - 2.6 | % | ASTM D955 |
| 23°C | 0.97 - 2.3 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.59 - 1.3 | % | ASTM D570 |
| 23°C, 24 hr | 0.82 - 1.7 | % | ISO 62 |
| Saturated, 23°C | 0.10 - 8.6 | % | ASTM D570 |
| Saturated, 23°C | 7.9 - 8.6 | % | ISO 62 |
| Equilibrium, 23°C | 0.81 - 2.8 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 - 2.9 | % | ISO 62 |
| Viscosity Number | 134 - 150 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 78 - 122 | ASTM D785 | |
| 23°C | 55 - 122 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 70 - 83 | ASTM D2240 | |
| 23°C | 78 - 93 | ISO 868 | |
| Ball Indentation Hardness | 67.4 - 166 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 805 - 6860 | MPa | ASTM D638 |
| 23°C | 707 - 7760 | MPa | ISO 527-2 |
| -- | 4880 | MPa | ISO 527-2 1 |
| Tensile Strength | |||
| Yield, 23°C | 44.1 - 90.5 | MPa | ASTM D638 |
| Yield, 23°C | 38.3 - 91.3 | MPa | ISO 527-2 |
| Yield | 65.3 | MPa | ISO 527-2 2 |
| Fracture, 23°C | 39.3 - 126 | MPa | ASTM D638 |
| Fracture, 23°C | 34.8 - 169 | MPa | ISO 527-2 |
| Fracture | 119 | MPa | ISO 527-2 3 |
| Limit, 23°C | 79.2 - 83.7 | MPa | ASTM D638 |
| 23°C | 37.6 - 88.1 | MPa | ASTM D638 |
| 23°C | 39.5 - 139 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.0 - 14 | % | ASTM D638 |
| Yield, 23°C | 1.3 - 22 | % | ISO 527-2 |
| Yield | 13 | % | ISO 527-2 4 |
| Fracture, 23°C | 0.75 - 440 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 16 | % | ISO 527-2 |
| Fracture | 3.8 - 10 | % | ISO 527-2 5 |
| Nominal Tensile Strain at Break (23°C) | 24 - 51 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 4300 | MPa | ISO 899-1 |
| 1000 hr | 3490 | MPa | ISO 899-1 |
| Flexural Modulus | |||
| 23°C | 1500 - 3750 | MPa | ASTM D790 |
| 23°C | 602 - 3600 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 49.7 - 139 | MPa | ASTM D790 |
| 23°C | 11.0 - 250 | MPa | ISO 178 |
| Yield, 23°C | 44.0 - 200 | MPa | ASTM D790 |
| Fracture, 23°C | 56.5 - 211 | MPa | ASTM D790 |
| Compressive Strength | |||
| 23°C | 30.3 - 193 | MPa | ASTM D695 |
| 23°C | 24.0 - 110 | MPa | ISO 604 |
| Shear Strength (23°C) | 65.0 - 85.3 | MPa | ASTM D732 |
| Poisson's Ratio (23°C) | 0.40 - 0.42 | ASTM E132 | |
| Coefficient of Friction | 0.056 - 0.37 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 4.00 - 24.0 | mg | ASTM D1044 |
| Wear Factor | 11 - 400 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 39.2 - 59.5 | J/m | ASTM D256 |
| 23°C | 1.2 - 26 | kJ/m² | ISO 179 |
| 23°C | 14.3 | kJ/m² | ISO 179/1eA 6 |
| Charpy Unnotched Impact Strength | |||
| 23°C | 44 - 110 | kJ/m² | ISO 179 |
| 23°C | 77.5 | kJ/m² | ISO 179/1eU 7 |
| Notched Izod Impact | |||
| 23°C | 34 - 100 | J/m | ASTM D256 |
| 23°C | 2.5 - 24 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 3.00 - 15.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 40 - 1700 | J/m | ASTM D256 |
| 23°C | 19 - 140 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 31.0 - 70.0 | kJ/m² | ASTM D256 |
| Instrumented Dart Impact | |||
| 23°C | 0.570 - 76.0 | J | ASTM D3763 |
| 23°C | 0.700 - 67.8 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 816 - 5400 | N | ISO 6603-2 |
| Tensile Impact Strength (23°C) | 63.0 - 344 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 177 - 241 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 141 - 234 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 56.7 - 93.6 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.8 - 96.2 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 50.0 - 60.1 | °C | ISO 75-2/C |
| Continuous Use Temperature | 84.4 - 131 | °C | ASTM D794 |
| Vicat Softening Temperature | |||
| -- | 197 - 260 | °C | ASTM D1525 |
| -- | 198 - 252 | °C | ISO 306 |
| Ball Indentation Temperature | 189 - 191 | °C | IEC 60598-1 |
| Melting Temperature | |||
| -- | 254 - 260 | °C | |
| -- | 257 - 260 | °C | DSC |
| -- | 255 - 264 | °C | ISO 11357-3 |
| -- | 255 - 262 | °C | ASTM D3418 |
| -- | 260 - 262 | °C | ISO 3146 |
| Peak Crystallization Temperature (DSC) | 214 - 221 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | |||
| Flow | 5.6E-5 - 9.8E-5 | cm/cm/°C | ASTM D696 |
| Flow | 7.5E-5 - 1.4E-4 | cm/cm/°C | ASTM E831 |
| Flow | 6.7E-6 - 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 9.9E-5 - 1.3E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 7.0E-6 - 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1670 - 2100 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | |||
| 23°C | 0.20 - 1.8 | W/m/K | ASTM C177 |
| 23°C | 0.20 - 0.70 | W/m/K | ISO 8302 |
| RTI Elec | 65.0 - 131 | °C | UL 746 |
| RTI Imp | 65.0 - 96.9 | °C | UL 746 |
| RTI | 64.8 - 112 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 55 - 2.5E+15 | ohms | ASTM D257 |
| -- | 0.010 - 2.5E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 5.0 - 2.5E+16 | ohms·cm | ASTM D257 |
| 23°C | 0.10 - 2.5E+17 | ohms·cm | IEC 60093 |
| -- | 1.0E+10 - 1.0E+13 | ohms·m | IEC 60093 8 |
| Dielectric Strength | |||
| 23°C | 16 - 28 | kV/mm | ASTM D149 |
| 23°C | 15 - 45 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.05 - 5.53 | ASTM D150 | |
| 23°C | 2.90 - 10.2 | IEC 60250 | |
| 23°C | 4.41 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.010 - 0.20 | ASTM D150 | |
| 23°C | 3.0E-3 - 0.20 | IEC 60250 | |
| 1 MHz | 0.16 | IEC 60250 9 | |
| Arc Resistance | 118 - 150 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 588 - 600 | V | UL 746 |
| Comparative Tracking Index | |||
| -- | 595 - 609 | V | IEC 60112 |
| -- | 529 - 600 | V | ASTM D3638 |
| High Amp Arc Ignition (HAI) | 87.6 - 200 | UL 746 | |
| Hot-wire Ignition (HWI) | 20 - 93 | sec | UL 746 |
| Insulation Resistance (23°C) | 9.8E+11 - 1.0E+12 | ohms | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 99 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 642 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 - 28 | % | ASTM D2863, ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 0.75 - 15 | YI | ASTM D1925 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.8 - 90.6 | °C | |
| Drying Time | 2.7 - 5.3 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Dew Point | -18.1 - -17.8 | °C | |
| Suggested Max Moisture | 0.095 - 0.24 | % | |
| Suggested Shot Size | 50 - 60 | % | |
| Suggested Max Regrind | 23 | % | |
| Hopper Temperature | 70.0 - 270 | °C | |
| Rear Temperature | 257 - 303 | °C | |
| Middle Temperature | 270 - 302 | °C | |
| Front Temperature | 265 - 300 | °C | |
| Nozzle Temperature | 269 - 291 | °C | |
| Processing (Melt) Temp | 269 - 293 | °C | |
| Mold Temperature | 58.9 - 94.2 | °C | |
| Injection Pressure | 7.02 - 99.7 | MPa | |
| Holding Pressure | 40.9 - 97.5 | MPa | |
| Back Pressure | 0.138 - 2.63 | MPa | |
| Screw Speed | 45 - 101 | rpm | |
| Clamp Tonnage | 4.0 - 4.5 | kN/cm² | |
| Cushion | 4.68 - 5.04 | mm | |
| Vent Depth | 0.019 - 0.024 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66This information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.060 - 0.20 | % | |
| Cylinder Zone 1 Temp. | 272 - 285 | °C | |
| Cylinder Zone 2 Temp. | 273 - 285 | °C | |
| Cylinder Zone 3 Temp. | 271 - 298 | °C | |
| Cylinder Zone 4 Temp. | 273 - 303 | °C | |
| Melt Temperature | 283 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66This information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex A0520FNB02 | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| Sumitomo Epoxy EM 7302XLD | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| Torelina® A604 | Toray Resin Company | PPS | Torelina® |
| Axiall PVC 9113 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LOXIM 300 00 HB | LOXIM Industries Private Limited | Nylon 6 | LOXIM |