AvaSpire® AV-651 CF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V7l4Im_AvaSpire-AV-651-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AvaSpire AV -651 CF30 is a AvaSpire AV-651 30% carbon fiber reinforced brand. Compared with 30% carbon fiber reinforced PEEK, the formula has the advantages of better dimensional stability and more warpage resistance during injection molding. Among all AV-651 series materials, AV -651 CF30 brand has the highest strength, rigidity and fatigue resistance. In addition, this resin usually retains most of the useful ultra-high performance advantages of carbon fiber reinforced PEEK, including chemical resistance, fatigue resistance, and long-term thermal oxidation stability. The excellent balance performance of the AV- 651 CF30 makes it ideal for a wide range of applications including healthcare, transportation, electronics, oil and gas industries. This resin can be easily melt processed by injection molding on standard equipment. The melting treatment performance of AV-651 CF30 is generally very close to 30% carbon fiber reinforced PEEK. In the case of having the same performance characteristics as AV-651 CF30 and extruding at the same time, CF30 grade AV-621 low melt fluidity is considered to be more suitable for extruded products. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow : 3.18mm | 0.0 - 0.20 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.90 - 1.1 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 104 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 20700 | MPa | ASTM D638 |
| -- | 21100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 192 | MPa | ISO 527-2/1A/5 |
| -- 3 | 184 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 4 | 1.5 | % | ASTM D638 |
| Fracture | 1.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus | |||
| -- | 17200 | MPa | ASTM D790 |
| -- | 19100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 262 | MPa | ASTM D790 |
| -- | 280 | MPa | ISO 178 |
| Compressive Strength | 168 | MPa | ASTM D695 |
| Shear Strength | 94.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 59 | J/m | ASTM D256 |
| -- | 8.4 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| -- | 590 | J/m | ASTM D4812 |
| -- | 37 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(1.8 MPa, Annealed, 3.20 mm) | 212 | °C | ASTM D648 |
| Glass Transition Temperature | 158 | °C | ASTM D3418 |
| Peak Melting Temperature | 345 | °C | ASTM D3418 |
| CLTE - Flow (-50 to 50°C) | 8.2E-6 | cm/cm/°C | ASTM E831 |
| Specific Heat | DSC | ||
| 50°C | 1320 | J/kg/°C | DSC |
| 200°C | 1770 | J/kg/°C | DSC |
| Thermal Conductivity | 0.36 | W/m/K | ASTM E1530 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 540 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 366 | °C | |
| Middle Temperature | 371 | °C | |
| Front Temperature | 377 | °C | |
| Nozzle Temperature | 382 | °C | |
| Processing (Melt) Temp | 366 - 388 | °C | |
| Mold Temperature | 149 - 177 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| 保压压力：最低值 |
| Note Message | |
|---|---|
| 1 . | 5" x 0.5" x 0.125" bars |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 200°C,2 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E F2201 | Asia Polymer Corporation (APC) | LDPE | Polymer-E |
| Sylvin 8217-88 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Colorite 11 Series 9011 | Colorite Polymers | PVC, Unspecified | Colorite 11 Series |
| KOCETAL® WR301LOBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| EPAMOULD 687A10 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |