OnForce™ LFT LF5200-5001 FR Black

Category:	Polyolefin, Unspecified , Polyolefin
Manufacturer:	PolyOne Corporation
Trademark:	OnForce™ LFT
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	V7Iepb_OnForce-LFT-LF5200-5001-FR-Black.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.

General Information
Filler / Reinforcement	Long glass fiber
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.50	g/cm³	ISO 1183
Molding Shrinkage ¹	0.25	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	12000	MPa	ISO 527-2
Tensile Stress (Break)	85.0	MPa	ISO 527-2
Tensile Strain (Break)	1.0	%	ISO 527-2
Flexural Modulus	10800	MPa	ISO 178
Flexural Stress	135	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	14	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	30	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	154	°C	ISO 75-2/A
8.0 MPa, not annealed	140	°C	ISO 75-2/C

Flammability	Nominal Value	Unit	Test Method
Flammability Classification (1.60 to 3.20 mm)	V-0		IEC 60695-11-10, -20
Glow Wire Flammability Index (1.60 to 3.20 mm)	960	°C	IEC 60695-2-12

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Processing (Melt) Temp	210 - 230	°C
Mold Temperature	60.0	°C
Injection Rate	Slow-Moderate
Back Pressure	1.00	MPa

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Note Message
1 .	Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processingconditions.

Resin Grade	Manufacturer	Category	Trademark
PRE-ELEC® TPE 1504	Premix Oy	TPE	PRE-ELEC®
Trexprene® D50BW	Mitsubishi Chemical Performance Polymers, Inc.	TPV	Trexprene®
BJB Polyurethane TC-892 FR REV 1	BJB Enterprises, Inc.	PUR, Unspecified	BJB Polyurethane
AR® 1	Greene, Tweed & Co.	TP, Unspecified	AR®
Crastin® SK605 NC010	DuPont Performance Polymers	PBT	Crastin®