omay® U42B
| Category: | Film, PC , PC Film |
| Manufacturer: | Suzhou OMAY Optical Materials Co., Ltd |
| Trademark: | omay® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V5Z4oL_omay-U42B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Surface Tension | > 38 | mN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | 2B - B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 100 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 152 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 156 | °C | ISO 11357 |
| CLTE - Flow | 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM D5470 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 VTM-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® H517-25RG | Safripol (PTY) LTD | PP Homopolymer | Safron® |
| NEXT SIGNATURE PPH G30-300 | NEXT Specialty Resins, Inc. | PP Homopolymer | NEXT SIGNATURE |
| ADENE NCWB | A.D. Compound spa | PP Homopolymer | ADENE |
| Lucolit® 1310 | Lucobit AG | TPO (POE) | Lucolit® |
| Integra™ 9060 FR | PolySource, LLC | PK | Integra™ |