LNP™ THERMOCOMP™ DF004P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V56YFr_LNPTHERMOCOMPDF004Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF004P is a Polycarbonate base resin containing Glass Fiber. Characteristics of this grade are Exceptional Processing. Also known as: LNP* THERMOCOMP* Compound DF-1004 EP BK8-115 Product reorder name: DF004P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10900 | MPa | ASTM D638 |
| -- | 6340 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.0 | MPa | ASTM D638 |
| Yield | 28.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 106 | MPa | ASTM D638 |
| Fracture | 102 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 1.6 | % | ASTM D638 |
| Fracture | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 5 | 6400 | MPa | ASTM D790 |
| -- 6 | 12500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 202 | MPa | ISO 178 |
| Fracture, 50.0mm span 7 | 156 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 91 | J/m | ASTM D256 |
| 23°C 8 | 7.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 740 | J/m | ASTM D4812 |
| 23°C 9 | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 97.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX-EN-FR3 | Polymer Resources Ltd. | PPE+PS | PRL |
| RheTech Polypropylene T20P200-01BG | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sylvin 2817-80 White 1475 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Mylar® D (200 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| EGYPTENE HD 5218 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |