TAROMID A 280 H MG6 DX0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V4ZX6N_TAROMID-A-280-H-MG6-DX0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 medium viscosity, 30% mineral fiber reinforced, UL94 V0 self extinguishing, Material PBDE/PBDF free. UL94 V0 approved - NC@ 0,75 mm Available: all colours, UV-stabilised (L), heat-stabilised (H), release agent (W), elastomer modified (R). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 to 1.60 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.65 | % | |
| Across Flow | 0.65 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.50 | % | ASTM D570, ISO 62 |
| Saturation | 4.5 | % | ASTM D570 |
| Saturation, 23°C | 4.5 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 50 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 232 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | 130 | °C | UL 746B |
| Vicat Softening Temperature | |||
| -- | 254 | °C | ASTM D1525, ISO 306/A50 3 1 |
| -- | 242 | °C | ASTM D1525, ISO 306/B50 4 2 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 2.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (Solution A) | > 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 8001 | Formosa Plastics Corporation | HDPE | TAISOX |
| ACCUTECH™ HP0336W30L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Kumho SSBR SOL-5270H | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| Lumid® GP2430B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |
| LUVOCOM® 19-7277 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |