Geon™ Vinyl Rigid Extrusion L0111
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V133rl_Geon-Vinyl-Rigid-Extrusion-L0111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon™Vinyl Rigid Extrusion L0111 is a rigid PVC product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: food contact applications. The main characteristics are: accessible food. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 13453 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2790 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 49.2 | MPa | ASTM D638 |
| Flexural Modulus | 2870 | MPa | ASTM D790 |
| Flexural Strength | 85.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 23°C, 3.18mm, injection molding | 85 | J/m | ASTM D256A |
| Transverse flow : 23°C, 3.18mm, molded | 43 | J/m | ASTM D256A |
| Flow : 23°C, 3.18mm, molded | 32 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 60.9 | J/cm | ASTM D4226 |
| 23°C 4 | 192 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 67.8 | °C | ASTM D648 |
| CLTE - Flow | 6.7E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| 注释：分档是采用注塑模制样品进行缺口摆锤冲击试验确定的。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BIPEX B0620FN17 | Ginar Technology Co., LTD. | PBT | BIPEX |
| Arnitel® EL250 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| LNP™ THERMOCOMP™ RFB71S compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |
| Sumiliteresin® PR-53804 BI | SBHPP | Phenolic | Sumiliteresin® |
| 3M™ Dyneon™ PTFE Compound PDR 04004 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |