INLUBE PPSCF30TF15
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INLUBE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V0ur7v_INLUBE-PPSCF30TF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% CARBON FIBER REINFORCED/ 15% PTFE LUBRICATED POLYPHENYLENE SULFIDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.050 to 0.20 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 162 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 to 2.0 | % | ASTM D638 |
| Flexural Modulus | 19300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 263 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+2 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 7.6E-3 to 0.013 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 FR UV | RTP Company | PP, Unspecified | RTP |
| Moplen Z11G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Utomer UT81P90A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| OMIKRON BE 7042 NERO | TECNOPOL | PP Homopolymer | OMIKRON |
| POCAN® BF 4409 000000 | LANXESS Corporation | PBT | POCAN® |