LNP™ STAT-KON™ FX98500C compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UyxpnU_LNP-STAT-KON-FX98500C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON FX98500C is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-F-98500 Product reorder name: FX98500C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.976 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.7 to 3.0 | % | |
| Across Flow : 24 hr | 1.9 to 2.2 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1080 | MPa | ASTM D638 |
| -- | 871 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 23.9 | MPa | ASTM D638 |
| Yield | 23.0 | MPa | ISO 527-2 |
| Break | 13.9 | MPa | ASTM D638 |
| Break | 14.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 16 | % | ASTM D638 |
| Yield | 14 | % | ISO 527-2 |
| Break | 43 | % | ASTM D638 |
| Break | 83 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 870 | MPa | ASTM D790 |
| -- | 931 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 26.5 | MPa | ASTM D790 |
| -- | 27.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 21.4 | J | ASTM D3763 |
| -- | 63.2 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 46.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 48.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+5 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 232 | °C | |
| Mold Temperature | 37.8 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIC3702 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Semi-Rigid | Sinvicomp |
| CGPC PVC SO-30X (125 phr Plasticizer F) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Grilon® BG-30/2 | EMS-GRIVORY | Nylon 6 | Grilon® |
| Karina RED PVC COMP. -E 850-42/231-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9703-66 Yellow 4167 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |