Greenflex® FF 45
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Greenflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UxeQb4_Greenflex-FF-45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greenflex FF 45 is an ethylene vinyl acetate copolymer (EVA) suitable for blown film extrusion. Films produced with Greenflex FF 45 show high toughness. Main Application Greenflex FF 45 is recommended for the production of greenhouse film, stretch hood packaging and sanitary applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 14.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Injection Molded | 92 | ||
| Shore D, Injection Molded | 39 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 50 to 200 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 65.0 | MPa | |
| 1% Secant, TD : Blown Film | 70.0 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 6.00 | MPa | |
| TD : Yield, Blown Film | 5.00 | MPa | |
| MD : Break, Blown Film | 31.0 | MPa | |
| TD : Break, Blown Film | 29.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 450 | % | |
| TD : Break, Blown Film | 700 | % | |
| Dart Drop Impact 1(Blown Film) | 700 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 24.0 | kN/m | |
| TD | 40.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 73.0 | °C | ISO 306/A |
| Melting Temperature | 93.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 80 | ASTM D2457 | |
| Haze (Blown Film) | 1.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ OLP80 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| RAMOFIN PPC501 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| SUSTAVACU 6 GF | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAVACU |
| Nanjing Hongrui PBT T306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| Sylvin 2900-70 Clear 8382 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |