EXCELLOY SX220
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | EXCELLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Uvx54t_EXCELLOY-SX220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXCELLOY SX220 is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in North America or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 104 | ASTM D785 | |
| R scale | 104 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 43.1 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2350 | MPa | ASTM D790 |
| -- | 2150 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 71.6 | MPa | ASTM D790 |
| -- | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179 |
| Notched Izod Impact | 250 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 96.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 82.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 95.0 | °C | |
| Drying Time | 2.0 - 5.0 | hr | |
| Rear Temperature | 190 - 260 | °C | |
| Middle Temperature | 190 - 260 | °C | |
| Front Temperature | 190 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-709P | CHI MEI CORPORATION | ABS | POLYLAC® |
| Medalist® MD-16376 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist® |
| Keltan® 5470P | LANXESS Buna GmbH | EPDM | Keltan® |
| Iupiace® LN60 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LOXIM 840 02T HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |