Iupilon® MB9000
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UvvOEr_IupilonMB9000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Polymer Alloy (PC/ABS)-2
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Lateral flow : 3.20mm | 0.25 - 0.45 | % | |
| Traffic : 3.20mm | 0.25 - 0.45 | % | |
| Water Absorption (Saturation, 23°C) | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 63 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 24 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 86.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 78.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.0 mm | V-1 | UL 94 | |
| 1.5 mm | 5VB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 200 - 240 | °C | |
| Middle Temperature | 210 - 250 | °C | |
| Front Temperature | 220 - 270 | °C | |
| Nozzle Temperature | 220 - 270 | °C | |
| Mold Temperature | 50 - 70 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA TA-35 | Mitsubishi Rayon America Inc. | ASA+PC | Shinko-Lac® |
| Braskem PP C7069-100NA | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| ELASTEL™ CR-FR-5 | HELLENIC CABLES S.A. | PCR | ELASTEL™ |
| Generic SAS | Generic | SAS | Generic |
| NYLOY® CM-5000 8325B6 | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |